使用万能拉力试验机TY800（江都市天源试验机械有限公司）对制备得到的木聚糖增韧聚氨酯样条进行力学性能测试。木聚糖增韧聚氨酯制备工艺：R-48型羟基丙烯酸树脂（中海油常州涂料化工研究院）：乙酸丁酯（国药化学试剂有限公司）=2:1（质量比）混合均匀，加入5 wt.%（以R-48型羟基丙烯酸树脂质量计）低聚木糖3#样品搅拌12h，加入50 wt.%（以R-48型羟基丙烯酸树脂计）六亚甲基二异氰酸酯（中海油常州涂料化工研究院），超声搅拌均匀，滴加二丁基锡二月桂酸催化剂（中海油常州涂料化工研究院），拉膜。

The mechanical properties of the prepared xylan toughened polyurethane spline were tested by the universal tensile testing machine TY800 (Jiangdu Tianyuan Testing Machinery Co., LTD.). Xylan toughened polyurethane preparation process: R-48 type hydroxyl acrylic resin (CNOOC Changzhou Coating Chemical Research Institute) : Butyl acetate (Sinopodal Chemical Reagent Co., LTD.) =2:1 (mass ratio) mixed evenly, adding 5 wt.% (R-48 hydroxyl acrylic resin mass) xylooligosaccharide 3# sample stirring for 12h, adding 50 wt.% (R-48 hydroxyl acrylic resin) hexamethylene diisocyanate (CNOOC Changzhou Coating Chemical Research Institute), Ultrasonic stirring, drop dibutyltin dilauric acid catalyst (CNOOC Changzhou Coating Chemical Research Institute), pull the film.