(a)右图显示涂层缺陷的深度为343.11 μm，左图显示涂层缺陷的长度为3.5 cm；(b)低表面能修复液对高表面能环氧树脂涂层(HSES)修复。右图显示在高表面能基板使用低表面能环氧树脂修复后，修复后缺陷深度为146.83 μm；(c)低表面能修复液对低表面能环氧树脂涂层(LSES)修复。右显示在低表面能基板使用低表面能环氧树脂修复后，涂层缺陷的深度为149.34 μm

(a) The depth of the coating defect shown on the right is 343.11 μm, and the length of the coating defect shown on the left is 3.5 cm; (b) Repair of high surface energy epoxy coating (HSES) with low surface energy repair solution. The figure on the right shows that after the high surface energy substrate was repaired with low surface energy epoxy resin, the defect depth after repair was 146.83μm. (c) Low surface energy repair solution for low surface energy epoxy coating (LSES) repair. Shown on the right is a coating defect depth of 149.34μm on a low surface energy substrate repaired with a low surface energy epoxy resin